Milled Glass is by E-glass fiber strand through crushing, grinding and screening process and made a very short fibers. The product has good dispersion and not change the resin liquid, is a good filling material of thermosetting and thermoplastic resin to improve surface crack phenomenon, reduce the mold and good heat resistance to friction materials. Also can be used as shock reinforced material. Widely used in all kinds of thermosetting and thermoplastic resin.
Application:
l Filling material
l Lacquer putty material
l Reinforced material
l High-performance friction material
l Laminate crack
Specification:
Milled Glass | |
Glass Type | E-Glass |
Filament Diameter | 9-14μm |
Glass Spectific Gravity | 2.60g/cm3 |
Colour | White |
Softening Temperature | 840°C |
Moisture | <0.3% |
Surface Treatment | Silane |
LOl | 0.3-1.5% |
Tensile Strength | 70-120Cn/tex |
Elongation at Break | 3400N/mm2 |
Modulus | 2800-3400cN/tex |
*Specific products could be made according to customers’requirements.
Available Products:
Product Code | EMG-50 | EMG-100 | EMG-200 | EMG-400 |
Average Fiber Length(μm) | ≈50 | ≈100 | ≈200 | ≈300 |
Longest Fiber Length(μm) | ≈1000 | ≈1000 | ≈1000 | ≈2000 |
Appearance | Powdery | Powdery | Slight Flocculent | Flocculent |
Bulk Density(kg/l) | ≈0.7 | ≈0.6 | ≈0.35 | ≈0.26 |
0.65-0.75 | 0.50-0.65 | 0.3-0.4 | 0.25-0.28 | |
Measured Fiber Length<125μm | >60 | >55 | >30 | |
Measured Fiber Length<250μm | >60 | >55 | >30 | |
Measured Fiber Length<1000μm | ≈100 | |||
Flowability | Good | Good | Average | Poor |
Thermal Deformation Temperature(PA-6)°C | ≈100 | ≈160 |